The role of drying-control chemical additives on the preparation of sol-gel derived PLZT thin films

De An Chang, Yi Hung Choh, Wen Feng Hsieh, Pang Lin, Tseung-Yuen Tseng*

*Corresponding author for this work

研究成果: Article同行評審

23 引文 斯高帕斯(Scopus)

摘要

Films of Pbx/100Lax/100(Zry/100Tiz/100)1-x/400O3 with x=8, y=65 and z=35 (PLZT(8/65/35)) with a single perovskite structural phase were successfully prepared by using drying-control chemical additives in sol-gel processing followed by rapid thermal annealing at 600 °C for only 1 min on Si(Pt) substrates. The roles of the drying-control chemical additives ethylene glycol and formamide in the gel preparation were studied. The hysteresis loop of PLZT(8/65/35) thin film was measured. The remanent polarization and coercive field were found to be about 1.3 μC cm-2 and 15 kVcm-1, respectively.

原文English
頁(從 - 到)6691-6698
頁數8
期刊Journal of Materials Science
28
發行號24
DOIs
出版狀態Published - 1 一月 1993

指紋 深入研究「The role of drying-control chemical additives on the preparation of sol-gel derived PLZT thin films」主題。共同形成了獨特的指紋。

引用此