Synthesis of thermal-stable and photo-crosslinkable polyfluorenes for the applications of polymer light-emitting diodes

Pei Hsuan Wang, Ming Shou Ho, Sheng-Hsiung Yang, Kuei Bai Chen, Chain-Shu Hsu*

*Corresponding author for this work

研究成果: Article同行評審

21 引文 斯高帕斯(Scopus)

摘要

Three polyfluorene derivatives which have oxetanecontaining phenyl group at C-9 position were synthesized via the palladium-catalyzed Suzuki-coupling reaction. The synthesized polymers PFB, PFG, and PFR emit blue, green, and red light, respectively. A double-layer device with the configuration of ITO/PEDOT/polymer/Ca/AI using PFB as the active layer showed a threshold voltage of 5 V, a maximum brightness of 2030 cd/m2, and a maximum current efficiency of 0.35 cd/A. Using PFG as the active layer, the device exhibited a threshold voltage of 6 V, a maximum brightness of 6447 cd/m2, and a maximum current efficiency of 1.27 cd/A. Using PFR as the active layer, the device showed a threshold voltage of 4 V, a maximum brightness of 2135 cd/m2, and a maximum current efficiency of 0.16 cd/A. Better electroluminescent performance was also found based on different design of device structures. Due to photo-crosslinking property of oxetane groups, the UVexposed thin films are insoluble In common organic solvents. A device comprised of blue, green, and red-emissive pixels was successfully fabricated by spin-coating and photo-lithographic processes. In addition, a white light-emitting device with CIE coordinate of (0.34, 0.33) was achieved by blending PFR into a host material PFB as the active layer.

原文English
頁(從 - 到)516-524
頁數9
期刊Journal of Polymer Science, Part A: Polymer Chemistry
48
發行號3
DOIs
出版狀態Published - 1 二月 2010

指紋 深入研究「Synthesis of thermal-stable and photo-crosslinkable polyfluorenes for the applications of polymer light-emitting diodes」主題。共同形成了獨特的指紋。

引用此