Synthesis and characterization of alkali-metal tin(II) phosphates: Na10Sn31(HPO4)6(P2O7)6(PO4)12 and K2SnP2O7

Sheng Feng Weng, Kuei Bo Chen, Chi-Shen Lee*

*Corresponding author for this work

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)


Two new alkali-metal tin(II) phosphates - Na10Sn31(HPO4)6(P2O7)6(PO4)12 (1) and K2SnP2O7 (2) - were synthesized by high-temperature reactions and structurally characterized by single-crystal X-ray diffraction. Na10Sn31(HPO4)6(P2O7)6(PO4)12 crystallized in the noncentrosymmetric space group P-62c (No. 190) with a = 9.6445(1) Å, b = 9.6445(1) Å, c = 34.059(6) Å, V = 2743.6(7) Å3 and Z = 1. K2SnP2O7 crystallized in the monoclinic space group P21/n with a = 9.856(3) Å, b = 6.7244(1) Å, c = 12.225(3) Å, β = 108.240(5)°, V = 769. 5(3) Å3 and Z = 4. Both structures exhibit a novel open-framework structure. The crystal structure of 1 contains SnO3 and SnO4 polyhedra sharing corners with [HPO4]2-, [PO4]3- and [P2O7]4- groups, which form tunnels of six rings filled with Na+ cations and parallel to the c-axis, which are connected via O-Sn-O bridges to form a three-dimensional open framework. The crystal structure of 2 contains SnO4 seesaw polyhedra sharing corners with diphosphate groups to form a three-dimensional [SnP2O7]2- framework that exhibits a tunnel structure of 10- and 12-membered rings expanding along [011] and [100] with four arrays of K+ cations located in channels of the framework.

頁(從 - 到)1485-1490
期刊Solid State Sciences
出版狀態Published - 1 十一月 2008

指紋 深入研究「Synthesis and characterization of alkali-metal tin(II) phosphates: Na<sub>10</sub>Sn<sub>31</sub>(HPO<sub>4</sub>)<sub>6</sub>(P<sub>2</sub>O<sub>7</sub>)<sub>6</sub>(PO<sub>4</sub>)<sub>12</sub> and K<sub>2</sub>SnP<sub>2</sub>O<sub>7</sub>」主題。共同形成了獨特的指紋。