Structural, dielectric and Mossbauer studies of PbFe0.5Sb0.5O3 ceramics with differing degree of compositional ordering

I. P. Raevski*, A. V. Pushkarev, S. I. Raevskaya, N. M. Olekhnovich, Yu V. Radyush, S. P. Kubrin, Haydn Chen, C. C. Chou, D. A. Sarychev, V. V. Titov, M. A. Malitskaya

*Corresponding author for this work

研究成果: Article同行評審

12 引文 斯高帕斯(Scopus)

摘要

Ceramic samples of a new perovskite multiferroic PbFe0.5Sb0.5O3 (PFS) with a differing degree S of long-range compositional ordering of the Fe3+ and Sb5+ cations were fabricated by a variation of the high-pressure-synthesis conditions. The S values estimated from the XRD data varied from 0.93 down to 0.17. The unit cell parameter was found to decrease with increasing S. In line with these results the fraction of the singlet component in the Mössbauer spectra was found to decrease with decreasing S. However, the temperatures and diffusion of dielectric permittivity maxima as well as the temperature of magnetic phase transition determined from Mössbauer data do not change substantially with S. These results imply that PFS remains highly ordered at the nanoscale.

原文English
頁(從 - 到)154-164
頁數11
期刊Ferroelectrics
501
發行號1
DOIs
出版狀態Published - 1 九月 2016

指紋 深入研究「Structural, dielectric and Mossbauer studies of PbFe<sub>0.5</sub>Sb<sub>0.5</sub>O<sub>3</sub> ceramics with differing degree of compositional ordering」主題。共同形成了獨特的指紋。

引用此