Sintering of (Ca1-x, Mgx)Zr4(PO4)6 ceramics

Dean-Mo LIu*

*Corresponding author for this work

研究成果: Article同行評審

15 引文 斯高帕斯(Scopus)

摘要

Densification and grain growth of (Ca1-x, Mgx)Zr4(PO4)6 (CMZP; where x=0.0, 0.1, and 0.4) ceramics at the intermediate stage of sintering have been investigated. A lattice-diffusion model proposed by Coble with tetrakaidecahedron as a grain shape was employed and appears to be applicable to the sintering of CMZP. The apparent diffusion coefficient of the CMZP ceramics for x=0.0 is lower by approximately three and one orders of magnitude than for x=0.1 and x=0.4, respectively. The grain growth in CMZP at the intermediate stage of sintering follows a third-power kinetics, i.e. n=3. A modified expression using the lattice-diffusion model associated with grain-growth kinetics has been derived which makes the microstructures of CMZP controllable.

原文English
頁(從 - 到)1507-1513
頁數7
期刊Journal of Materials Science
29
發行號6
DOIs
出版狀態Published - 1 一月 1994

指紋 深入研究「Sintering of (Ca<sub>1-x</sub>, Mg<sub>x</sub>)Zr<sub>4</sub>(PO<sub>4</sub>)<sub>6</sub> ceramics」主題。共同形成了獨特的指紋。

引用此