Shallow n+p junction formation by implanting P+ ions into thin Co films and laser processing

Huang-Chung Cheng*, M. H. Juang

*Corresponding author for this work

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

Effects of laser annealing (LA) on the formation of silicided shallow junctions have been studied. The junctions are made by P+ implantation into thin Co films on Si substrate and subsequent drive-in/silicidation. Various implant and annealing conditions are examined. Conventional furnace annealing (CFA) is also undertaken. Good junctions can be achieved only by using low-temperature CFA due to the severe diffusion of knock-on Co atoms at high temperatures. The junctions formed by LA processing are poor in this scheme. However, the junctions formed by CFA only show small change of the dopant redistribution and the Co penetration after a subsequent LA. In addition, the silicide crystallinity and the junction characteristics can be further improved using a proper LA power. The results indicate that the laser-recrystallization technique is a promising technique for the fabrication of three-dimensional devices.

原文English
頁(從 - 到)124-129
頁數6
期刊Materials Chemistry and Physics
33
發行號1-2
DOIs
出版狀態Published - 1 一月 1993

指紋 深入研究「Shallow n<sup>+</sup>p junction formation by implanting P<sup>+</sup> ions into thin Co films and laser processing」主題。共同形成了獨特的指紋。

引用此