Resistive switching mechanisms of V-doped SrZrO3 memory films

Chun Chieh Lin, Bing Chung Tu, Chao Cheng Lin, Chen Hsi Lin, Tseung-Yuen Tseng

研究成果: Article同行評審

84 引文 斯高帕斯(Scopus)

摘要

The resistive switching behaviors of sputtered V-doped SrZrO3 (V:SZO) memory films were investigated in this letter. The current states of the memory films were switched between high current state (H-state) and low current state (L-state). The resistance ratio of the two current states was over 1000 at a read voltage. The switching mechanism from L- to H-state corresponds to the formation of current paths. However, this mechanism from H- to L-state is thought to be due to the fact that the defects present in the V:SZO film randomly trap electrons, and hence, the current paths are ruptured. The conduction mechanism of the H-state is dominated by ohmic conduction, whereas the L-state conduction is dominated by Frenkel-Poole emission. The polarity direction of the resistive switching is an intrinsic property of the SrZrO3 oxides. The V:SZO films with high uniformity and good stability are expected to be used in nonvolatile memory.

原文English
頁(從 - 到)725-727
頁數3
期刊IEEE Electron Device Letters
27
發行號9
DOIs
出版狀態Published - 1 九月 2006

指紋 深入研究「Resistive switching mechanisms of V-doped SrZrO<sub>3</sub> memory films」主題。共同形成了獨特的指紋。

引用此