Mechanical properties of three-dimensional ordered macroporous Ni foam

Chen Hong Liao, Pei Sung Hung, Yu Cheng, Shou Yi Chang, Pu-Wei Wu*

*Corresponding author for this work

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

We employ a sequential electrophoresis and electrodeposition approach to fabricate a large-area ordered macroporous Ni foam in 5 × 5 cm2 via a template route. Images from scanning electron microscope exhibit hierarchical structures with hexagonally-arranged pores and interconnected pore channels. For as-prepared and annealed ordered macroporous Ni foams, the loading-depth profiles from nano indentation show typical elastic and plastic deformation. Upon annealing, moderate growth in grain size is observed, resulting in lower hardness and Young's modulus. In contrast, for disordered macroporous Ni foam and solid Ni film, nano indentation results reveal larger hardness and undetermined Young's modulus. The ordered macroporous foam reveals hardness that is 22% of that of solid Ni film, a value close to its theoretic packing density of 24%.

原文English
頁(從 - 到)152-156
頁數5
期刊Materials Letters
215
DOIs
出版狀態Published - 15 三月 2018

指紋 深入研究「Mechanical properties of three-dimensional ordered macroporous Ni foam」主題。共同形成了獨特的指紋。

引用此