Low-Temperature Activation and Recrystallization of B+- and BF+2-Implanted LPCVD Amorphous-Si Films

Huang-Chung Cheng, Fang Shing Wang, Yeong Fang Huang, Chun Yao Huang

研究成果: Article同行評審

3 引文 斯高帕斯(Scopus)

摘要

Low-temperature (600°C) activation and recrystallization of the low-pressure chemical vapor deposition (LPCVD) amorphous-Si films B+- and BFJ-implanted with different implantation dosages and projection ranges have been investigated. The boron dopant in the amorphous-Si layer can enhance the recrystallization, resulting in the shorter incubation time and smaller grain size then the undoped specimens. For the BFJ-implanted specimens, the existence of fluorine atoms could postpone the grain nucleation, leading to the longer incubation time and slower nucleation rate for the heavily doped specimens than the undoped ones. For the BFJ-implanted specimens, as the implantation peak reaches to the ct-Si/Si02 interface, the recoiled oxygen atoms from the oxide substrate would retard the grain nucleation and exhibit a significantly large grain size after a long time annealing. However, the recoiled oxygen atoms and the microdefects in the poly-Si layers would offset the improvement in hole mobility. Higher hole mobilities and lower trap state densities were also observed for the BFJ-implanted specimens with respect to the B+-implanted ones. It is attributed to the passivation effect of fluorine atoms within the poly-Si layers.

原文English
頁(從 - 到)3574-3578
頁數5
期刊Journal of the Electrochemical Society
142
發行號10
DOIs
出版狀態Published - 1 一月 1995

指紋 深入研究「Low-Temperature Activation and Recrystallization of B+- and BF+2-Implanted LPCVD Amorphous-Si Films」主題。共同形成了獨特的指紋。

引用此