LC mixture with promoted electro-optical properties for LCD applications by using a highly UV-resistant dopant

Shih Hsien Liu, Po Jen Yang, Hong-Cheu Lin*

*Corresponding author for this work

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

A highly ultraviolet (UV)-resistant dopant 3HBBTfV consisting of an a-trifluomethyl vinylbenzene (TfV) moiety was synthesized and mixed with a commercial LC host (A) to promote its dielectric anisotropy in LC mixture C (A:3HBBTfV = 9:1 w/w). Their electric-optical properties were studied and compared with those of an analogous commercial LC mixture B composed of LC mixture A (as a commercial host) mixed with the same weight ratio (10% wt.) of a commercial component 3HBEBTf containing a 3,4,5-trifluorobenzene (BTf) moiety. The electro-optical properties of voltage holding ratio (VHR) values and voltage-transmission (V-T) curves of LC mixture C were sustained after the UV irradiation. These results showed that dopant 3HBBTfV (acting as an UV stabilizer) demonstrated a higher stability under UV exposure in contrast to commercial component 3HBEBTf. Therefore, LC mixture C (containing UV-resistant dopant 3HBBTfV) exhibited good UV resistance, high dielectric anisotropy, and excellent electro-optical properties.

原文English
頁(從 - 到)764-773
頁數10
期刊Optical Materials Express
5
發行號4
DOIs
出版狀態Published - 1 一月 2015

指紋 深入研究「LC mixture with promoted electro-optical properties for LCD applications by using a highly UV-resistant dopant」主題。共同形成了獨特的指紋。

引用此