Investigation of the interactions between titanium and calcium zirconium oxide (CaZrO3) ceramics modified with alumina

Ming Wei Lu, Kun Lin Lin, Chien-Cheng Lin*

*Corresponding author for this work

研究成果: Article同行評審

3 引文 斯高帕斯(Scopus)

摘要

Powdered mixtures of CaO, ZrO2 and Al2O3 in various ratios were hot pressed. The mixtures reacted with titanium at 1600 °C for 30 min in argon to evaluate the suitable ceramic crucibles for casting of titanium. The interfacial microstructures between titanium and ceramic composites were characterized using X-ray diffrac-tometer, scanning and transmission electron microscope. The produced hot pressed mixtures that were chemically bonded together, contained calcium aluminate (CaAl2O4), calcium dialuminate (CaAl4O7), cubic zirconia (c-ZrO2), and calcium zirconium oxide (CaZrO3). The increase in Al2O3 amount led to the decrease in CaZrO3 amount and an increase in the amount of CaAl2O4, CaAl4O7 and c-ZrO2 due to the reaction of CaO and Al2O3. At the end of the reaction of the ceramic mixtures with Ti at 1600 °C for 30 min, the acicular α-Ti and β-Ti were formed at the interface of Ti and the composites containing up to 10 vol.% Al2O3. In composites containing more than 20 vol.% Al2O3, Ti3Al5 was found at the interface instead of α-Ti and β-Ti. Furthermore, CaZrO3, ZrO2 and Ca3Al2O6 existed on the sides of the ceramic far away from the interface. CaZrO3/Al2O3 composites with less than 20 vol.% Al2O3 could be a potential crucible or mould material for productive applications in titanium casting.

原文English
頁(從 - 到)79-88
頁數10
期刊Processing and Application of Ceramics
13
發行號1
DOIs
出版狀態Published - 1 一月 2019

指紋 深入研究「Investigation of the interactions between titanium and calcium zirconium oxide (CaZrO<sub>3</sub>) ceramics modified with alumina」主題。共同形成了獨特的指紋。

引用此