Interfacial reactions in In/Cu2Se couples

Sinn wen Chen*, Hsin-Jay Wu, Che wei Hsu, Cheng I. Chang, Chun fei Chang

*Corresponding author for this work

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

In/Cu2Se couples were reacted at 623K and 723K for 1800-14,400s. In4Se3 and non-planar finger-type CuInSe2 were formed at the In/Cu2Se interface. The η-Cu2In phase was formed with longer reaction time. In addition to these phases formed at the interfaces, precipitates of CuInSe2 formed in the Cu2Se substrate and chunky CuInSe2 phase formed at the end of the Cu2Se substrate. Results in the In/Cu2Se/Ni couple reacted at 723K show that the reaction phases at the In/Cu2Se interface and the CuInSe2 precipitates in the Cu2Se substrate are the same, but there is no chunky CuInSe2 phase at the Cu2Se end adjacent to Ni. The CuInSe2 precipitates in the Cu2Se substrate are formed due to supersaturation of indium caused by a decrease in solubility at lower temperatures. The non-planar morphology of the CuInSe2 phase at the interface is caused by the fast diffusion of indium, the segregation and preferred facet growth of the CuInSe2 phase. However, the mechanism for the formation of the chunky CuInSe2 is not clear and further study is required.

原文English
頁(從 - 到)402-406
頁數5
期刊Journal of the Taiwan Institute of Chemical Engineers
44
發行號3
DOIs
出版狀態Published - 1 二月 2013

指紋 深入研究「Interfacial reactions in In/Cu<sub>2</sub>Se couples」主題。共同形成了獨特的指紋。

引用此