Influence of stearic acid on suspension structure and green microstructure of injection-molded zirconia ceramics

Wenjea J. Tseng, Dean-Mo LIu, Chung King Hsu

研究成果: Article同行評審

55 引文 斯高帕斯(Scopus)

摘要

The effect of stearic acid (added as a surfactant and/or a lubricant) on powder dispersion and particle packing of a zirconia ceramic/binder system has been investigated. Microstructural examination revealed that the addition of stearic acid prevented the particles from making a direct surface-to-surface contact. Contrarily, an insufficient coverage of the acid onto the powder surface resulted in a formation of particulate networks and led to an increase in suspension viscosity. A significant reduction in the most frequent pore size of the thermally debound samples was found as the fraction of stearic acid exceeded 3 wt% on the basis of powder loading. This corresponds to a nominal > 90% of surface coating by the adsorbed acid before being blended with the wax/polymer as a binder. The acid adsorption gradually reached a plateau as the acid increases above 3 wt%. High acid quantities (> 5 wt%) are detrimental to the molding integrity as cracks were observed during thermal removal of the binder.

原文English
頁(從 - 到)191-195
頁數5
期刊Ceramics International
25
發行號2
DOIs
出版狀態Published - 1 一月 1999

指紋 深入研究「Influence of stearic acid on suspension structure and green microstructure of injection-molded zirconia ceramics」主題。共同形成了獨特的指紋。

引用此