Highly efficient poly(3,4-ethylenedioxythiophene): Poly(styrenesulfonate)/ Si hybrid solar cells with imprinted nanopyramid structures

Jheng Yuan Chen, Ming Hung Yu, Shun Fa Chang, Kien-Wen Sun*

*Corresponding author for this work

研究成果: Article

33 引文 斯高帕斯(Scopus)

摘要

High-efficiency hybrid solar cells based on nanostructured silicon and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate), which were fabricated via a simple nanoimprint fabrication process, demonstrated an excellent power conversion efficiency of 10.86%. The complex and costly high-temperature photolithography and masking steps were replaced by techniques that are low-cost and capable of mass production. The nanopyramid structures fabricated on the silicon surface provided an antireflective effect and have a radial junction architecture that enhanced the light absorption and carrier collection efficiency. The short-circuit current density (Jsc) of the hybrid solar cell with nanopyramid structures was greatly improved from 24.5 mA/cm 2 to 32.5 mA/cm2 compared with that of a flat surface device. The highest solar cell efficiency was achieved on a 525 μm-thick 2.3 Ω cm n-type Czochralski process (CZ) Si substrate with a designated area of 4 cm2.

原文English
文章編號133901
期刊Applied Physics Letters
103
發行號13
DOIs
出版狀態Published - 23 九月 2013

指紋 深入研究「Highly efficient poly(3,4-ethylenedioxythiophene): Poly(styrenesulfonate)/ Si hybrid solar cells with imprinted nanopyramid structures」主題。共同形成了獨特的指紋。

  • 引用此