Growth of optical-quality, uniform In-rich InGaN films using two-heater metal-organic chemical vapor deposition

S. F. Fu, C. Y. Chen, F. W. Li, C. H. Hsu, Wu-Ching Chou, Wen-Hao Chang, Wei-Kuo Chen*, W. C. Ke

*Corresponding author for this work

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

Good-optical-quality, thick InxGa1-xN films with high In content were grown using a homemade two-heater metal-organic chemical vapor deposition system. By varying the growth temperature, it was found that the In composition of the InGaN epilayer varied from 18 to 59% as the substrate temperature decreased from 750 to 625 C. Our results show that the optical properties in terms of the emission peak wavelength and linewidth are uniformly distributed throughout the entire 2 in. wafer for the x=0.40 InGaN sample. The resultant mean peak wavelength and FWHM are 808±6 nm and 229±18 meV, respectively, at 18 K. In addition, for the InGaN film grown at 625 C, a noticeable decrease in the In composition occurred when the ceiling temperature was >800 C, indicative of the occurrence of parasitic reactions in the gas phase.

原文English
頁(從 - 到)106-111
頁數6
期刊Journal of Crystal Growth
383
DOIs
出版狀態Published - 30 九月 2013

指紋 深入研究「Growth of optical-quality, uniform In-rich InGaN films using two-heater metal-organic chemical vapor deposition」主題。共同形成了獨特的指紋。

引用此