Growth evolution of SixNy on the GaN underlayer and its effects on GaN-on-Si (111) heteroepitaxial quality

Tzu Yu Wang, Sin Liang Ou, Ray-Hua Horng, Dong Sing Wuu*

*Corresponding author for this work

研究成果: Article

15 引文 斯高帕斯(Scopus)

摘要

The GaN epilayers were grown on Si(111) substrates via combining the techniques of AlN buffer, the graded AlGaN structure and the Si xNy interlayer by metalorganic chemical vapor deposition. The SixNy interlayers with various growth times of 0-60 s were introduced into the growth of GaN epilayers. To thoroughly realize the growth evolution of SixNy, measurements of atomic force microscopy, field emission scanning electron microscopy and nano-Auger electron spectroscopy were performed. From the measurement by transmission electron microscopy, it can be proven that nanocrystalline SixNy is preferentially located at the dislocation cores and pits during the growth process. For the fabrication of GaN/graded AlGaN/AlN/Si, the full width at half maximum of the X-ray diffraction rocking curve at the GaN(102) plane was reduced effectively from 965 to 771 arcsec by inserting SixNy into the GaN epilayer, which resulted from the bending and annihilation of dislocations.

原文English
頁(從 - 到)5724-5731
頁數8
期刊CrystEngComm
16
發行號25
DOIs
出版狀態Published - 7 七月 2014

指紋 深入研究「Growth evolution of Si<sub>x</sub>N<sub>y</sub> on the GaN underlayer and its effects on GaN-on-Si (111) heteroepitaxial quality」主題。共同形成了獨特的指紋。

  • 引用此