Growth and physical characterization of polygon prismatic hollow Zn-ZnO crystals

Kun Ho Liu, Chin Ching Lin, San-Yuan Chen*

*Corresponding author for this work

研究成果: Article同行評審

22 引文 斯高帕斯(Scopus)

摘要

A hierarchical polygon prismatic Zn-ZnO core-shell structure was grown on silicon by combining liquid-solution colloidals together with the vapor-gas growth process. Zn colloidals with a diameter of 5-10 nm synthesized from Zn(ClO4)2 precursor solution were used as nucleation seeds for the growth of Zn polygon prismatic nanocrystals. Depending on carrier gas and annealing conditions, the polygon prismatic Zn crystals having morphology from hollow to dense configuration can be manipulated. Moreover, after prolonged thermal treatment at 300-400 °C, polygon prismatic hollow ZnO-Zn crystals with a dimension from nanometer to micrometer can be obtained. The room-temperature photoluminescence spectra show that the hollow ZnO-Zn crystals have a weak ultraviolet (UV) emission at 380 nm and a strong green emission at 500 nm. However, the intensity of the UV emission can be improved by postannealing the Zn-ZnO core-shell structure in an oxygen atmosphere to form hollow ZnO crystals.

原文English
頁(從 - 到)483-487
頁數5
期刊Crystal Growth and Design
5
發行號2
DOIs
出版狀態Published - 1 三月 2005

指紋 深入研究「Growth and physical characterization of polygon prismatic hollow Zn-ZnO crystals」主題。共同形成了獨特的指紋。

引用此