Formation of TiSi2 on nitrogen ion implanted (001)Si

S. L. Cheng*, L. J. Chen, Bing-Yue Tsui

*Corresponding author for this work

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

Formation of TiSi2 on nitrogen ion implanted (001)Si has been investigated. Nitrogen ion implantation was found to suppress the B and As diffusion in silicon. For Ti on 30 keV BF2+-20 keV N2+ and 30 keV As+-20 keV N2+ implanted samples, a continuous low-resistivity TiSi2 layer was found to form in all samples annealed at 700-900 °C. For Ti on 1 × 1015/cm2 N2+- and As+ implanted samples, end-of-range defects were completely eliminated in all samples annealed at 700-900 °C. The results indicated that with appropriate control, N+-implantation can be successfully implemented in forming low-resistivity TiSi2 contacts on shallow junctions in deep submicron devices.

原文English
頁(從 - 到)213-221
頁數9
期刊Journal of Materials Research
14
發行號1
DOIs
出版狀態Published - 1 一月 1999