Field emission of vertically aligned V2O5 nanowires on an ITO surface prepared with gaseous transport

Ming Cheng Wu, Chi-Shen Lee*

*Corresponding author for this work

研究成果: Article同行評審

37 引文 斯高帕斯(Scopus)

摘要

Growing V2O5 nanowires (NWs) on a conducting glass substrate combines gaseous transport and pyrolytic deposition of vanadium polyoxometalate anions, and yields vertically aligned vanadium-oxide nanowires. Scanning electron and transmission electron microscopy, selected-area electron diffraction, Raman spectra and powder X-ray analyses indicate that V2O5 nanowires as synthesized were single-crystalline and grew anisotropically among direction [010]. NH2OH·HCl served not only as a reducing agent to produce vanadium polyoxometalate clusters but also as a source of NH3 gas to facilitate the vapor pyrolysis and deposition. The optical properties of V2O5 nanowires exhibit a character dependent on structure. Field emission (FE) measurements show a small turn-on field voltage ~8.3 V/μm, maximum current density 1.8 mA/cm2, and a linear Fowler-Nordheim behavior.

原文English
頁(從 - 到)2285-2289
頁數5
期刊Journal of Solid State Chemistry
182
發行號8
DOIs
出版狀態Published - 1 八月 2009

指紋 深入研究「Field emission of vertically aligned V<sub>2</sub>O<sub>5</sub> nanowires on an ITO surface prepared with gaseous transport」主題。共同形成了獨特的指紋。

引用此