Fabrication and Properties of DC—Sputtered Tl-1223 Superconducting Thin Films

Jenh-Yih Juang, J. H. Horng, H. C. Lin, C. M. Fu, T. M. Uen, Y. S. Gou

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

A multi-step deposition and post annealing scheme has been developed for preparing nearly single phase, c-axis oriented TlBa2Ca2Cu3Og (Tl-1223) superconducting thin films by dc-sputtering. The effects of the compensates used during post annealing on final phase formation suggest the crucial role played by thermodynamic conditions and further validates the viability of the present process scheme. In particular, films obtained by the present process have shown, for the first time in this system, a critical current density (Jc) above 106 A/cm2at 77 K with a zeroresistance transition temperature (Tco) above 110 K. The results are attributed to the improvement of film morphology, specifically a decreased density of weak-links.

原文English
文章編號402901
頁(從 - 到)1689-1692
頁數4
期刊IEEE Transactions on Applied Superconductivity
5
發行號2
DOIs
出版狀態Published - 六月 1995

指紋 深入研究「Fabrication and Properties of DC—Sputtered Tl-1223 Superconducting Thin Films」主題。共同形成了獨特的指紋。

引用此