Evaluation of AlGaN/GaN metal-oxide-semicondutor high-electron mobility transistors with plasma-enhanced atomic layer deposition HfO2/AlN date dielectric for RF power applications

Yu Sheng Chiu, Quang Ho Luc, Yueh Chin Lin, Jui Chien Huang, Chang Fu Dee, Burhanuddin Yeop Majlis, Edward Yi Chang

研究成果: Article同行評審

摘要

A plasma enhanced atomic layer deposition (PEALD) HfO2/AlN dielectric stack was used as the gate dielectric for AlGaN/GaN metal-oxide-semiconductor high-electron-mobility transistors (MOS-HEMTs) for high-frequency power device applications. The capacitance-voltage (C-V) curves of the HfO2/AlN/GaN MOS capacitor (MOSCAP) showed a small frequency dispersion along with a very small hysteresis (>50 mV). Moreover, the interface trap density (Dit) was calculated to be 2.7 ' 1011 cm%2 V%1 s%1 at 150 °C. Using PEALD-AlN as the interfacial passivation layer (IPL), the drain current of the HfO2/AlN MOS-HEMTs increased by about 46% and the gate leakage current decreased by six orders of magnitude as compared with those of the conventional Schottky gate AlGaN/GaN HEMTs processed using the same epitaxial wafer. The 0.3-µm-gate-length HfO2/AlN/AlGaN/GaN MOS-HEMTs demonstrated a 2.88 W/mm output power, a 23 dB power gain, a 30.2% power-added efficiency at 2.4 GHz, and an improved device linearity as compared with the conventional AlGaN/GaN HEMTs. The third-order intercept point at the output (OIP3) of the MOS-HEMTs was 28 4 as compared with that of 26 5 for the conventional GaN HEMTs Overall the MOS-HEMTs with a HfO /AlN gate stack showed good potential for high-linearity RF power device applications.

原文English
文章編號094101
期刊Japanese Journal of Applied Physics
56
發行號9
DOIs
出版狀態Published - 1 一月 2017

指紋 深入研究「Evaluation of AlGaN/GaN metal-oxide-semicondutor high-electron mobility transistors with plasma-enhanced atomic layer deposition HfO<sub>2</sub>/AlN date dielectric for RF power applications」主題。共同形成了獨特的指紋。

引用此