Enhancing efficiency for additive–free blade–coated small–molecule solar cells by thermal annealing

Pei Ting Tsai, Hsin-Fei Meng*, Yongsheng Chen, Bin Kan, Sheng Fu Horng

*Corresponding author for this work

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

Blade coating was successfully applied to realise high-efficiency small-molecule organic solar cells (OSCs) with a solution-processed active layer comprising a small organic molecule DR3TBDTT with a benzo[1,2–b:4,5–b′]dithiophene (BDT) unit as the central building block as the donor and [6,6]–phenyl–C71–butyric acid methyl ester (PC71BM) as the acceptor. Using chloroform as the solvent, a DR3TBDTT/PC71BM blend active layer without an additive was effectively formed through blade coating. The power conversion efficiency (PCE) of small organic molecule solar cells was enhanced by 3.7 times through thermal annealing at 100 °C. This method produces OSCs with a high PCE of up to 6.69%, with an open circuit voltage (Voc) of 0.97 V, a short-circuit current density (Jsc) of 12.60 mA/cm2, and a fill factor (FF) of 0.55.

原文English
頁(從 - 到)305-311
頁數7
期刊Organic Electronics
37
DOIs
出版狀態Published - 1 十月 2016

指紋 深入研究「Enhancing efficiency for additive–free blade–coated small–molecule solar cells by thermal annealing」主題。共同形成了獨特的指紋。

引用此