Effects of platinum doping on the photoelectrochemical properties of Fe2O3 electrodes

Ya Ping Hsu, Sheng Wei Lee, Jeng-Kuei Chang, Chung Jen Tseng*, Kan Rong Lee, Chih Hao Wang

*Corresponding author for this work

研究成果: Article同行評審

20 引文 斯高帕斯(Scopus)

摘要

The effects of platinum (Pt) doping on the structure and photoelectrochemical properties of Fe2O3electrodes have been investigated. The Pt-doped Fe2O3 electrodes were prepared by sol-gel and spin coated on fluorine-tin-oxide coated glass substrate. Influences of dopant concentration on material properties and photoelectrochemical characteristics were examined. Results of XRD and XPS showed that α-Fe2O3 can be obtained using 500 oC annealing in air. The band gaps of the samples obtained from reflectance and transmittance spectra measurement were found to vary from 1.98 to 2.03 eV. Theflat band potentials of the samples were obtained from the Mott-Schottky analysis and found to be in the range of -0.135 V to -0.6 V. The maximum photocurrent density of undoped and 0.1 at.% Pt-doped Fe2O3 electrodes was 0.5 mA/cm2 and 0.7 mA/cm2 under a 300 W Xe lamp system, respectively. Thegood photoelectrochemical results of the Pt-doped Fe2O3 electrode warrant further investigation for broader applications in the future.

原文English
頁(從 - 到)11615-11623
頁數9
期刊International Journal of Electrochemical Science
8
發行號9
出版狀態Published - 30 九月 2013

指紋 深入研究「Effects of platinum doping on the photoelectrochemical properties of Fe<sub>2</sub>O<sub>3</sub> electrodes」主題。共同形成了獨特的指紋。

引用此