Competing magnetic interactions and interfacial frozen-spins in Ni-NiO core-shell nano-rods

Hao Chun Hsu, Chih Chieh Lo, Yuan-Chieh Tseng*

*Corresponding author for this work

研究成果: Article同行評審

13 引文 斯高帕斯(Scopus)

摘要

This paper investigates the subtle interfacial magnetism of highly-aligned, free-standing Ni-NiO core-shell rods on a Si substrate, fabricated by electroless-plating and an anodic aluminum oxide template. Transmission electron microscopy found that the NiO shell was uniformly present along the entire rod. Vertical magnetization shift, arising from opposite field cooling conditions, suggests frozen spins (FS) at the Ni-NiO interface. The FS were related to the pinning effects of the NiO on the Ni. The pinning strength depended on the NiO thickness, displaying a tunable fashion from 6 to 10 nano-meters with thermal annealing. The FS mediated the antiferromagnetic (AFM)-ferromagnetic (FM) interfacial coupling, leading to the temperature-dependent properties of the rods. FS were evident below 100 K, at which the NiO-AFM dominated the properties with a suppressed coercive field and non-saturated magnetization. At 100 K, however, the Ni-FM was superior to the NiO-AFM with a restored FM phase. Meanwhile, the interfacial magnetic frustration occurred due to the disappearance of FS. These two factors resulted in the coercivity enhancement at 100 K. The uniqueness of the structure opens opportunities to tailoring the properties of the rods by manipulating the core-shell inter-dependency, as well as inspiring further researches concerning its applications in spintronics.

原文English
文章編號063919
期刊Journal of Applied Physics
111
發行號6
DOIs
出版狀態Published - 15 三月 2012

指紋 深入研究「Competing magnetic interactions and interfacial frozen-spins in Ni-NiO core-shell nano-rods」主題。共同形成了獨特的指紋。

引用此