Characterization of semi-polar (20 2 ¯ 1) InGaN microLEDs

Ray-Hua Horng*, Shreekant Sinha, Yuh Renn Wu, Fu Guo Tarntair, Jung Han, Dong Sing Wuu

*Corresponding author for this work

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

In this paper, semi-polar (202 ¯ 1) InGaN blue light-emitting diodes (LEDs) were fabricated and compared the performance with those of LEDs grown on c-plane sapphire substrate. LEDs with different chip sizes of 100 μm × 100 μm, 75 μm × 75 μm, 25 μm × 25 μm, and 10 μm × 10 μm were used to study the influence of chip size on the device performance. It was found that the contact behavior between the n electrode and the n-GaN layer for the semi-polar (202 ¯ 1) LEDs was different from that for the LEDs grown on the c-plane device. Concerning the device performance, the smaller LEDs provided a larger current density under the same voltage and presented a smaller forward voltage. However, the sidewall’s larger surface to volume ratio could affect the IQE. Therefore, the output power density reached the maximum with the 25 μm × 25 μm chip case. In addition, the low blue-shift phenomenon of semi-polar (202 ¯ 1) LEDs was obtained. The larger devices exhibited the maximum IQE at a lower current density than the smaller devices, and the IQE had a larger droop as the current density increased for the LEDs grown on c-plane sapphire substrate.

原文English
文章編號15966
頁數9
期刊Scientific reports
10
發行號1
DOIs
出版狀態Published - 1 十二月 2020

指紋 深入研究「Characterization of semi-polar (20 2 ¯ 1) InGaN microLEDs」主題。共同形成了獨特的指紋。

引用此