Anisotropic characteristics of in-plane aligned a-axis YBa2Cu3O7-δ thin films

Chih-Wei Luo, M. H. Chen, C. C. Chiu, Kaung-Hsiung Wu, Jenh-Yih Juang, T. M. Uen, Jiunn-Yuan Lin, Y. S. Gou

研究成果: Article同行評審

8 引文 斯高帕斯(Scopus)

摘要

Highly in-plane aligned a-axis oriented YBa2 Cu3 O7-δ (YBCO) thin films with unprecedented transition temperature (Tc ∼ 91.3 K) have been deposited on (100) LaSrGaO4 substrates using a continuously grown PrBa2 Cu3 O7-δ (PBCO) template layer by pulsed laser. The anisotropies between b- and c-axis were investigated by transport measurements and atomic force microscopy (AFM . Although, the onset Tc's along b- and c-axis appeared approximately the same, a significant filing was observed in the resistive transition along c-axis. The temperature-dependent of the tailing effect, however, cannot be explained by thermally activated phase-slippage (TAPS) commonly encountered in grain-boundary weak links.

原文English
頁(從 - 到)545-550
頁數6
期刊Journal of Low Temperature Physics
131
發行號3-4
DOIs
出版狀態Published - 1 五月 2003

指紋 深入研究「Anisotropic characteristics of in-plane aligned a-axis YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> thin films」主題。共同形成了獨特的指紋。

引用此