A facile surface treatment utilizing binary mixtures of ammonium salts and polar solvents for multiply enhancing thermoelectric PEDOT: PSS films

Tsung Che Tsai, Tsung Han Chen, Hsiu Cheng Chang, Chun-Hua Chen, Yi Chia Huang, Wha Tzong Whang*

*Corresponding author for this work

研究成果: Article

9 引文 斯高帕斯(Scopus)

摘要

A novel composite recipe coupling binary mixtures of the 2-methoxyethanol (ME) solvent and ammonium salt, which has respectively proven as the electrical conductivity and Seebeck coefficient enhancers, was for the first time introduced for treating the surface of baked poly(3,4ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) films. The pristine film of PH 1000 is prepared by evenly spreading commercial PEDOT:PSS solution onto the cleaned glass substrates with a subsequent baking process. Hundred microliter of pure ME or mixtures of ME and single ammonium salt, ammonium formate (AF) or ammonium nitrate (AN), was dropped onto the baked pristine PEDOT:PSS films and then the surface coated film was spun at 2000 rpm and dried at 120°C for 1 h. The present remarkable enhancement in the resulting dimensionless figure-of-merit (ZT) is evidenced as the result of the phase separation brought by ME and the dedoping effect brought by AF, which leads to the optimization of the electrical conductivity and Seebeck coefficient, respectively.

原文English
頁(從 - 到)3303-3306
頁數4
期刊Journal of Polymer Science, Part A: Polymer Chemistry
52
發行號23
DOIs
出版狀態Published - 1 一月 2014

指紋 深入研究「A facile surface treatment utilizing binary mixtures of ammonium salts and polar solvents for multiply enhancing thermoelectric PEDOT: PSS films」主題。共同形成了獨特的指紋。

  • 引用此