Rate of consumption of Cu in soldering accompanied by ripening

H. K. Kim*, King-Ning Tu

*Corresponding author for this work

Research output: Contribution to journalArticle

109 Scopus citations

Abstract

What is the rate of consumption of Cu in soldering reactions has been a critical question in electronic packaging technology. The Cu films are consumed by Cu-Sn compound formation. Because the Cu thickness is limited and the rework of a solder joint requires a layer of unreacted Cu, the loss of Cu in soldering must be under control. At the solder interface, Cu-Sn intermetallic compounds do not form layered structures. Rather, the Cu6Sn5 phase grows as scalloplike grains into the molten solder and ripening occurs between the grains. Therefore, it has been difficult to determine the compound growth rate, and in turn the Cu consumption rate. Using cross-sectional and top-polished samples, we have measured the total volume of Cu-Sn intermetallic compounds formed between eutectic SnPb alloy and Cu substrate as a function of reflow time and temperature. We have deduced that after 1 min reflow, for example, the thickness of Cu consumed was about 0.36, 0.47, and 0.69 μm at 200, 220, and 240°C, respectively.

Original languageEnglish
Number of pages1
JournalApplied Physics Letters
Volume67
DOIs
StatePublished - 1 Dec 1995

Fingerprint Dive into the research topics of 'Rate of consumption of Cu in soldering accompanied by ripening'. Together they form a unique fingerprint.

  • Cite this