Nanotribological properties of ALD-processed bilayer TiO2/ZnO films

Wun Kai Wang, Hua Chiang Wen, Chun Hu Cheng, Ching-Hua Hung, Wu-Ching Chou, Wei Hung Yau*, Ping Feng Yang, Yi Shao Lai

*Corresponding author for this work

Research output: Contribution to journalArticle

4 Scopus citations

Abstract

TiO2/ZnO films grown by atomic layer deposition (ALD) demonstrated nanotribological behaviors using scratch testing. TEM profiles obtained an amorphous structure TiO2 and nanocrystalline structure ZnO, whereas the sample has significant interface between the TiO2/ZnO films. The experimental results show the relative XRD peak intensities are mainly contributed by a wurtzite oxide ZnO structure and no signal from the amorphous TiO2. With respect to tribology, increased friction causes plastic deformation between the TiO2 and ZnO films, in addition to delamination and particle loosening. The plastic deformation caused by adhesion and/or cohesion failure is reflected in the nanoscratch traces. The pile-up events at a loading penetration of 30 nm were measured at 21.8 μN for RT, 22.4 μN for 300°C, and 36 μN for 400°C. In comparison to the other conditions, the TiO2/ZnO films annealed at 400°C exhibited higher scratch resistance and friction with large debris, indicating the wear volume is reduced with increased annealing temperature and loading.

Original languageEnglish
Pages (from-to)2754-2759
Number of pages6
JournalMicroelectronics Reliability
Volume54
Issue number12
DOIs
StatePublished - 1 Dec 2014

Keywords

  • CVD coatings
  • Nanotribology
  • Scratch testing
  • Sliding friction

Fingerprint Dive into the research topics of 'Nanotribological properties of ALD-processed bilayer TiO<sub>2</sub>/ZnO films'. Together they form a unique fingerprint.

  • Cite this