Laser-induced decomposition and ablation dynamics studied by nanosecond interferometry: 3. A polyurethane film

Tomokazu Masubuchi*, Hiroshi Fukumura, Hiroshi Masuhara, Kenkichi Suzuki, Nobuaki Hayashi

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

18 Scopus citations

Abstract

A polyurethane sample film was prepared by adding phenol resin as a structural stabilizer and its laser ablation dynamics was studied upon excimer laser irradiation. The ablation threshold by 248nm excitation was determined to be 40mJ/cm2 and no appreciable debris was left. The etch depth increases with the fluence and reaches 0.5μm at the fluence of 1J/cm2. Time-resolved interferometric images were measured in the nanosecond to microsecond time region under surface and internal optical alignments. The film was decomposed efficiently into debris, fragments, aggregates, and so on which are smaller than the wavelength, as observed images were not disturbed by the decomposed products. At the fluence of 310mJ/cm2, etching proceeds fast during the initial half of the excitation laser pulse, but stopped at the late stage of the pulse. The direct measurement of transient absorbance change at 248nm explains that ejected products still absorb the excitation photons and interrupt a further etching. Laser-induced expansion was not observed above the ablation threshold, while below the value an expansion forms a bump and followed by rapid contraction. The morphological behavior is quite different from that of usual photothermal expansion and contraction dynamics observed for poly(methyl methacrylate) and polystyrene, hence it is considered that laser ablation is induced photochemically.

Original languageEnglish
Pages (from-to)215-222
Number of pages8
JournalJournal of Photochemistry and Photobiology A: Chemistry
Volume145
Issue number3
DOIs
StatePublished - 3 Dec 2001

Keywords

  • Laser ablation
  • Laser-induced expansion
  • Nanosecond interferometry
  • Photochemical decomposition
  • Polyurethane film

Fingerprint Dive into the research topics of 'Laser-induced decomposition and ablation dynamics studied by nanosecond interferometry: 3. A polyurethane film'. Together they form a unique fingerprint.

Cite this