Dielectric properties under dc-bias field of Ba0.6Sr0.4TiO3 with various grain sizes

Zhai Jiwei*, Yao Xi, Cheng Xiaogang, Zhang Liangying, H. D. Chen

*Corresponding author for this work

Research output: Contribution to journalArticle

22 Scopus citations


We study the effect of grain size on the dc field dependence of dielectric characteristics in Ba0.6Sr0.4TiO3 ceramics prepared by a sol-gel method. The samples were observed and analysed by SEM and X-ray diffraction. The dielectric constant samples decreases as the applied dc field increases. The influence of the dc field on the loss factor is much less than that on the dielectric constant. With increasing of the applied voltage, the Tc was increased and the peaks were suppressed and broadened. As the grain size increases, The maximum dielectric constant and the percentage change of dielectric constant under a dc field increase. A transition broadening and shift of Tc are observed as grain size decreases.

Original languageEnglish
Pages (from-to)164-169
Number of pages6
JournalMaterials Science and Engineering B: Solid-State Materials for Advanced Technology
Issue number2-3
StatePublished - 1 Jun 2002


  • Ceramics
  • Electric field
  • Grain size
  • Tunability

Fingerprint Dive into the research topics of 'Dielectric properties under dc-bias field of Ba<sub>0.6</sub>Sr<sub>0.4</sub>TiO<sub>3</sub> with various grain sizes'. Together they form a unique fingerprint.

  • Cite this