Deep levels and a possible d-x-like center in molecular beam epitaxial in x al 1-x as

W. P. Hong*, S. Dhar, P. K. Bhattacharya, Albert Chin

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

79 Scopus citations

Abstract

The work reported here was performed in order to establish whether or not complex defects like the D-X center can be present in InAlAs. Dominant deep electron and hole traps in lattice-matched In 0.52 Al 0.48 As/InP have been identified and characterized. The traps have activation energies ranging from 0.25 to 0.95 eV. The electron traps have very large capture cross-sections,~10 -12 -10 -11 cm 2 , similar to attractive centers. The lattice-matched samples do not show any persistent photoconductivity effects at low temperatures. In strained In 1-x Al x As with 0.48 <x ≤ 0.57, an electron trap with a thermal ionization energy of 0.35 eV, a strong dependence of its concentration on donor doping and very small thermal capture cross-section, 10 18 cm 2 , is identified. These samples exhibit persistent photoconductivity. We believe this trap is similar to the D-X center commonly observed in Al x Ga 1-x As for x ≥ 0.28.

Original languageEnglish
Pages (from-to)271-274
Number of pages4
JournalJournal of Electronic Materials
Volume16
Issue number4
DOIs
StatePublished - 1 Jul 1987

Keywords

  • D-X center
  • Molecular Beam Epitaxy
  • Ternary alloys

Fingerprint Dive into the research topics of 'Deep levels and a possible d-x-like center in molecular beam epitaxial in <sub>x</sub> al <sub>1-x</sub> as'. Together they form a unique fingerprint.

Cite this